C-6
2019-06-30 14:36:28| Steel Grade | : | C-6 |
| Chemical Composition(％)|WC | : | 71.0～83.0 |
| Chemical Composition(％)|TiC | : | 7.0～13.0 |
| Chemical Composition(％)|TaC(NbC) | : | 2.0～12.0 |
| Chemical Composition(％)|Co | : | 4.4～10.0 |
| Density/(g/cm^3) | : | 12.0～12.9 |
| Hardness HRA | : | 90.9～92.5 |
| Bending Strength/MPa | : | 1550～1895 |
| Application | : | Used in steel processing in general |