C-6A
2019-06-30 14:36:28| Steel Grade | : | C-6A |
| Chemical Composition(％)|WC | : | 74.0～80.0 |
| Chemical Composition(％)|TiC | : | 4.0～8.0 |
| Chemical Composition(％)|TaC(NbC) | : | 3.0～12.0 |
| Chemical Composition(％)|Co | : | 7.0～10.0 |
| Density/(g/cm^3) | : | 12.4～12.8 |
| Hardness HRA | : | 90.4～92.0 |
| Bending Strength/MPa | : | 1725～2070 |
| Application | : | Used in steel processing in general |