AISI 321H

2018-05-10 20:37:53
We are Manufacturer and supplier high quality and best quotation for AISI 321H, If you are interested in AISI 321H, please feel free to contact with us for more detailed data of AISI 321H. We will serve you with honesty, integrity, and professionality. And specific features are as follows: Specific feature is as follows for reference
Steel Grade: AISI 321H| ASTM —| UNS S32109|Type: Austenitic
CHEMICAL COMPOSITION(AISI 321H): 
C(%) :        0.04~0.10
Si(%) :         ≤1.00
Mn(%) :         ≤2.00
P(%)≤:         0.04
S(%)≤:         ≤0.030
Cr(%) :         17.0~20.0
Ni(%) :         9.00~12.0
Mo(%) :         —
Other(%) :         Ti4×C≤0.60
MECHANICAL PROPERTIES AND HARDNESS (AISI 321H):
Variety②:         B,F     B④
Condition③:         HF+A     CF+A
Tensile Strength|σb/MPa :         515     620
Yield Strength|σ0.2/MPa :         205     310
Extensibility|δ(%) :         40     30
Reduction of Area|ψ(%) :         50      40
Hardness HRB :         —     —
Standard ASTM :        A276,A473      A276
Remark(AISI 321H): 
②, B─Bar;F─forging;P─Thick plate;Sh─Sheet;St─Strip;Pi,T─Pipe steel;S-Pi,T─Seamless Pipe steel; W-T─Welded Pipe;Sp─Shape;W─wire.
③, A─Annealing;HF─Hot Forging;CF--Cold Drawing.
④, The thickness or diameter is more than 13mm.
⑤, The thickness or diameter is more than 13mm.
⑥, The diameter is more than 4mm.
⑦, When the diameter of wire is under 3.96mm, the δ is25%, and ψ is 40%.
⑧, The cross section of forging is above 127mm, then the σb is 485Pa.
Please find the PDF for AISI 321H  

Introduction Stainless Steel (AISI 321H)
Stainless steel does not readily corrode, rust or stain with water as ordinary steel does. However, it is not fully stain-proof in low-oxygen, high-salinity, or poor air-circulation environments. There are different grades and surface finishes of stainless steel to suit the environment the alloy must endure. Stainless steel is used where both the properties of steel and corrosion resistance are required.
Stainless steel differs from carbon steel by the amount of chromium present. Unprotected carbon steel rusts readily when exposed to air and moisture. This iron oxide film (the rust) is active and accelerates corrosion by forming more iron oxide; and, because of the greater volume of the iron oxide, this tends to flake and fall away. Stainless steels contain sufficient chromium to form a passive film of chromium oxide, which prevents further surface corrosion by blocking oxygen diffusion to the steel surface and blocks corrosion from spreading into the metal's internal structure. Passivation occurs only if the proportion of chromium is high enough and oxygen is present.

Applications (AISI 321H)
Stainless steel’s resistance to corrosion and staining, low maintenance and familiar lustre make it an ideal material for many applications. The alloy is milled into coils, sheets, plates, bars, wire, and tubing to be used in cookware, cutlery, household hardware, surgical instruments, major appliances, industrial equipment (for example, in sugar refineries) and as an automotive and aerospace structural alloy and construction material in large buildings. Storage tanks and tankers used to transport orange juice and other food are often made of stainless steel, because of its corrosion resistance. This also influences its use in commercial kitchens and food processing plants, as it can be steam-cleaned and sterilized and does not need paint or other surface finishes.
HOT SALE: 
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH, ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400, X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321, NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418, 616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405, ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13,  AISI 321H

Special Steel, Tapping Machine, Cold Heading Machine Supplier in China-Copy Right By Hacer Technology