ASTM 302B

2018-05-16 20:35:32
We are Manufacturer and supplier high quality and best quotation for ASTM 302B, If you are interested in ASTM 302B, please feel free to contact with us for more detailed data of ASTM 302B. We will serve you with honesty, integrity, and professionality. And specific features are as follows: Specific feature is as follows for reference
Steel Grade: AISI 302B| ASTM 302B| UNS S30215|Type: Austenitic
CHEMICAL COMPOSITION(ASTM 302B): 
C(%) :        ≤0.15
Si(%) :         2.00~3.00
Mn(%) :         ≤2.00
P(%)≤:         0.045
S(%)≤:         0.03
Cr(%) :         17.0~19.0
Ni(%) :         8.00~10.0
Mo(%) :         —
Other(%) :         —
MECHANICAL PROPERTIES AND HARDNESS (ASTM 302B):
Variety②:         B,F     B④
Condition③:         HF十A     CF+A
Tensile Strength|σb/MPa :         515     620
Yield Strength|σ0.2/MPa :         205     310
Extensibility|δ(%) :         40     30
Reduction of Area|ψ(%) :         50      40
Hardness HRB :         A276,A473     A276
Standard ASTM :        A276,A473      A276
Remark(ASTM 302B): 
②, B─Bar;F─forging;P─Thick plate;Sh─Sheet;St─Strip;Pi,T─Pipe steel;S-Pi,T─Seamless Pipe steel; W-T─Welded Pipe;Sp─Shape;W─wire.
③, A─Annealing;HF─Hot Forging;CF--Cold Drawing.
④, The thickness or diameter is more than 13mm.
⑤, The thickness or diameter is more than 13mm.
⑥, The diameter is more than 4mm.
⑦, When the diameter of wire is under 3.96mm, the δ is25%, and ψ is 40%.
⑧, The cross section of forging is above 127mm, then the σb is 485Pa.
Please find the PDF for ASTM 302B  

Introduction Stainless Steel (ASTM 302B)
Stainless steel does not readily corrode, rust or stain with water as ordinary steel does. However, it is not fully stain-proof in low-oxygen, high-salinity, or poor air-circulation environments. There are different grades and surface finishes of stainless steel to suit the environment the alloy must endure. Stainless steel is used where both the properties of steel and corrosion resistance are required.
Stainless steel differs from carbon steel by the amount of chromium present. Unprotected carbon steel rusts readily when exposed to air and moisture. This iron oxide film (the rust) is active and accelerates corrosion by forming more iron oxide; and, because of the greater volume of the iron oxide, this tends to flake and fall away. Stainless steels contain sufficient chromium to form a passive film of chromium oxide, which prevents further surface corrosion by blocking oxygen diffusion to the steel surface and blocks corrosion from spreading into the metal's internal structure. Passivation occurs only if the proportion of chromium is high enough and oxygen is present.

Applications (ASTM 302B)
Stainless steel’s resistance to corrosion and staining, low maintenance and familiar lustre make it an ideal material for many applications. The alloy is milled into coils, sheets, plates, bars, wire, and tubing to be used in cookware, cutlery, household hardware, surgical instruments, major appliances, industrial equipment (for example, in sugar refineries) and as an automotive and aerospace structural alloy and construction material in large buildings. Storage tanks and tankers used to transport orange juice and other food are often made of stainless steel, because of its corrosion resistance. This also influences its use in commercial kitchens and food processing plants, as it can be steam-cleaned and sterilized and does not need paint or other surface finishes.
HOT SALE: 
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH, ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400, X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321, NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418, 616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405, ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13,  ASTM 302B