AISI 316
2020-04-12 20:11:44
|
|
|
|
|
Specification and Steel Grade |
: |
AISI 316 |
|
Type |
: |
Stainless Steel |
|
|
|
|
|
Main Chemical Compositions|(%) |
: |
C≤0.08，Cr16.0～18.0，Ni10.0～14.0，Mo2.0～3.0 |
|
|
|
|
|
Strength of Extension|σb/MPa |
: |
760～1690 |
|
Elasticity Modulus|E/GPa |
: |
190 |
|
Torsional Property|σb Min(%) |
: |
40 |
|
Rigidity Modulus|G/GPa |
: |
69 |
|
Hardness|HRC |
: |
35～45 |
|
Working Temperature|/℃ |
: |
290 |
|
Features and Use |
: |
Has good heat resistance, corrosion resistance is better than 302 steel.Used for high quality spring |
|
|
|
|
|
Remark: |
|
|
|
①, For helical compression spring or tension spring, the distorting stress should be 75% of σb minimum. |
|
②, It is the United States federal specification. |
|
|
|
|
|
|
|
|
AISI 316
2020-04-12 20:11:44
|
|
|
|
|
Specification and Steel Grade |
: |
AISI 316 |
|
Type |
: |
Stainless Steel |
|
|
|
|
|
Main Chemical Compositions|(%) |
: |
C≤0.08，Cr16.0～18.0，Ni10.0～14.0，Mo2.0～3.0 |
|
|
|
|
|
Strength of Extension|σb/MPa |
: |
760～1690 |
|
Elasticity Modulus|E/GPa |
: |
190 |
|
Torsional Property|σb Min(%) |
: |
40 |
|
Rigidity Modulus|G/GPa |
: |
69 |
|
Hardness|HRC |
: |
35～45 |
|
Working Temperature|/℃ |
: |
290 |
|
Features and Use |
: |
Has good heat resistance, corrosion resistance is better than 302 steel.Used for high quality spring |
|
|
|
|
|
Remark: |
|
|
|
①, For helical compression spring or tension spring, the distorting stress should be 75% of σb minimum. |
|
②, It is the United States federal specification. |
|
|
|
|
|
|
|
|