WStE255
2017-12-27 15:15:28
We are a professional manufacturer of WStE255, we can provide the third party inspection report and datasheet of WStE255 as round bar, square bar, flat steel and so on. Please send the inquiry to us if you are if you are interested in WStE255. We will serve you with honesty, integrity, and professional. The detail data as below follow:
Steel Grade: WStE255| Material No.: 1.0060| Equal Germany DIN: St60-2
CHEMICAL COMPOSITION(WStE255):
C(％)≤: 0.18
Si(％) : ≤0.40
Mn(％)≤: 0.50～1.30
P(％)≤: 0.035
S(％)≤: 0.03
N(％)≤: 0.02
Al(％) : 0.02
Cr(％)≤: 0.30②
Cu(％)≤: 0.2
Mo(％)≤: 0.08②
Ni(％)≤: 0.3
Nb(％)≤: 0.3
Ti(％)≤: —
V(％) : —
Nb+Ti+V(％)⑥: 0.05
MECHANICAL PROPERTIES (WStE255):
Tensile Strength|σb/Mpa(≤70mm): 360～480
Normal Temp Yield Strength|σ/Mpa (≤16mm): 225
Extensibility|δ5≥(％): 25
Flexual Center Dia Cold-bend Test(180℃/T⑥⑦): 1a
Sample Direction L/T⑧⑨ : L/T
Ballistic|αkv≥(J/cm^2)( +20℃): 55/31
Remark(WStE255):
①, It is European standard steel grade in parenthesis, it have been revised by DIN EN 10028-5+6(1997) and DIN EN 10113(1993).
②, The balance of Cr+Cu+Mo is under 0.45％.
③, When the steel have Cu element, then the Cu is under 0.70％.
④, When the steel have Ni element, then the Ni is under 0.85％.
⑤, When the steel have Ti element, then the Ti is under 0.20％.
⑥, a-->Testing sample thickness.
⑦, When the thickness is more than 70mm, the flexual center diameter is 0.5a.
⑧, The testing sample is V form according to ISO.
⑨, This result apply to the thickness which is from 10mm to 150mm, and it is average value of three samples.
Introduction low alloy structural steel (WStE255)
Low alloy structural steel is a kind of steel that is added to ordinary carbon steel by adding a small amount of trace alloying elements to make the steel properties change. It has better properties than ordinary carbon steel, and also has some special properties, such as high temperature resistance and low temperature resistance. This kind of alloy steel belongs to low alloy steel because the total amount of alloying elements in this steel is not much.
Low alloy steel includes weldable low alloy and high strength structural steel, low alloy weathering steel, low alloy steel for reinforcing bar, low alloy steel for railway, low alloy steel for mining and other low alloy steels.
Characteristic(WStE255)
(1) low carbon: its carbon content is not more than 0.20% due to the high requirements of toughness, weldability and cold forming.
(2) adding manganese - based alloy elements.
(3) adding additional elements such as niobium, titanium or vanadium: a small amount of Nb, Ti or V forms fine carbide or carbides in steel, which is conducive to obtaining fine ferrite grains and improving strength and toughness of steel.
In addition, adding a small amount of copper (less than 0.4%) and phosphorus (about 0.1%), can improve the corrosion resistance. The addition of a small amount of rare earth elements can be used to remove and degassing, to purify the steel and to improve the toughness and technological properties.
Application(WStE255)
It is mainly used in the manufacture of bridges, ships, vehicles, boilers, high pressure vessels, oil and gas pipelines, large steel structures, etc.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH,
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405,
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13, WStE255
Steel Grade: WStE255| Material No.: 1.0060| Equal Germany DIN: St60-2
CHEMICAL COMPOSITION(WStE255):
C(％)≤: 0.18
Si(％) : ≤0.40
Mn(％)≤: 0.50～1.30
P(％)≤: 0.035
S(％)≤: 0.03
N(％)≤: 0.02
Al(％) : 0.02
Cr(％)≤: 0.30②
Cu(％)≤: 0.2
Mo(％)≤: 0.08②
Ni(％)≤: 0.3
Nb(％)≤: 0.3
Ti(％)≤: —
V(％) : —
Nb+Ti+V(％)⑥: 0.05
MECHANICAL PROPERTIES (WStE255):
Tensile Strength|σb/Mpa(≤70mm): 360～480
Normal Temp Yield Strength|σ/Mpa (≤16mm): 225
Extensibility|δ5≥(％): 25
Flexual Center Dia Cold-bend Test(180℃/T⑥⑦): 1a
Sample Direction L/T⑧⑨ : L/T
Ballistic|αkv≥(J/cm^2)( +20℃): 55/31
Remark(WStE255):
①, It is European standard steel grade in parenthesis, it have been revised by DIN EN 10028-5+6(1997) and DIN EN 10113(1993).
②, The balance of Cr+Cu+Mo is under 0.45％.
③, When the steel have Cu element, then the Cu is under 0.70％.
④, When the steel have Ni element, then the Ni is under 0.85％.
⑤, When the steel have Ti element, then the Ti is under 0.20％.
⑥, a-->Testing sample thickness.
⑦, When the thickness is more than 70mm, the flexual center diameter is 0.5a.
⑧, The testing sample is V form according to ISO.
⑨, This result apply to the thickness which is from 10mm to 150mm, and it is average value of three samples.
Introduction low alloy structural steel (WStE255)
Low alloy structural steel is a kind of steel that is added to ordinary carbon steel by adding a small amount of trace alloying elements to make the steel properties change. It has better properties than ordinary carbon steel, and also has some special properties, such as high temperature resistance and low temperature resistance. This kind of alloy steel belongs to low alloy steel because the total amount of alloying elements in this steel is not much.
Low alloy steel includes weldable low alloy and high strength structural steel, low alloy weathering steel, low alloy steel for reinforcing bar, low alloy steel for railway, low alloy steel for mining and other low alloy steels.
Characteristic(WStE255)
(1) low carbon: its carbon content is not more than 0.20% due to the high requirements of toughness, weldability and cold forming.
(2) adding manganese - based alloy elements.
(3) adding additional elements such as niobium, titanium or vanadium: a small amount of Nb, Ti or V forms fine carbide or carbides in steel, which is conducive to obtaining fine ferrite grains and improving strength and toughness of steel.
In addition, adding a small amount of copper (less than 0.4%) and phosphorus (about 0.1%), can improve the corrosion resistance. The addition of a small amount of rare earth elements can be used to remove and degassing, to purify the steel and to improve the toughness and technological properties.
Application(WStE255)
It is mainly used in the manufacture of bridges, ships, vehicles, boilers, high pressure vessels, oil and gas pipelines, large steel structures, etc.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH,
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405,
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13, WStE255