20Mn6
2018-01-12 14:43:38
We are a professional manufacturer of 20Mn6, we can provide the third party inspection report and datasheet of 20Mn6 as round bar, square bar, flat steel and so on. Please send the inquiry to us if you are if you are interested in 20Mn6. We will serve you with honesty, integrity, and professional. The detail data as below follow:
Steel Grade: 20Mn6| Material No.: 1.1169
CHEMICAL COMPOSITION(20Mn6):
C(％) : 0.17～0.23
Si(％) : 0.30～0.60
Mn(％) : 1.30～1.60
P(％) : 0.035
S(％) : 0.035
Cr(％) : —
Ni(％) : —
V(％): —
Other(％) : —
HEAT TREATMENT (20Mn6):
Hot Working/℃: 1100～850
Normalizing/℃: 860～890
Quench/℃: 860～890Water
Temper/℃: 500～850
MECHANICAL PROPERTIES IN NORMAL OR LOW TEMP (20Mn6) Condition: -20℃
Tensile Strength|σb/MPa: 530
Yield Strength|σs≥/MPa: 315
Extensibility|δ5(％)≥: 20
Reduction of Area|ψ(％)≥: —
Ballistic|αkv(DVM)/J: —
Remark(20Mn6):
①, It is European standard in this table for lower temperature steel of Germany, and according to DIN-EN10028-1(2000)，DIN-EN10028-4(1994)，DIN-EN10222-3(1999)，DIN-EN10269(1999) etc.
②, The balance of Cr+Cu+Mo is under 0.50％.
Introduction low-temperature structural steel (20Mn6)
The total content of the alloy elements is 5% ~ 10%, and the microstructure depends on the heat treatment system. 9Ni steel is a typical steel type. There are two commonly used heat treatment systems. One is 900 tempered normalizing plus 790 tempering normalizing plus 570 tempering tempering, the other is 800 tempered water quenching plus 570 tempering. After quenching, the microstructure is low carbon horse low body. After normalizing, it is organized into low carbon martensite plus ferrite and a small amount of high carbon austenite. 9Ni steel has excellent toughness at low temperature under 196. The sensitivity of phosphorus to the tempering brittleness of 9Ni steel should be strictly controlled. 5Ni steel is mainly through the optimization of chemical composition and heat treatment method to control the three levels of organization, which is similar with the strength and toughness of 9Ni steel in 162 C and C 196 under low temperature.
The total content of alloying elements > 10%, for austenite, has very good toughness at low temperature, in 196 ~ 296 degrees Celsius temperature remains very high toughness. The chromium nickel austenite low temperature steel contains Cr18% and Ni9%, and the chromium free nickel austenite low temperature steel contains M23% to 26% and A1% - 4%, and the toughness of the low temperature steel is similar. It is generally used after solid solution treatment.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH,
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405,
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13, 20Mn6
Steel Grade: 20Mn6| Material No.: 1.1169
CHEMICAL COMPOSITION(20Mn6):
C(％) : 0.17～0.23
Si(％) : 0.30～0.60
Mn(％) : 1.30～1.60
P(％) : 0.035
S(％) : 0.035
Cr(％) : —
Ni(％) : —
V(％): —
Other(％) : —
HEAT TREATMENT (20Mn6):
Hot Working/℃: 1100～850
Normalizing/℃: 860～890
Quench/℃: 860～890Water
Temper/℃: 500～850
MECHANICAL PROPERTIES IN NORMAL OR LOW TEMP (20Mn6) Condition: -20℃
Tensile Strength|σb/MPa: 530
Yield Strength|σs≥/MPa: 315
Extensibility|δ5(％)≥: 20
Reduction of Area|ψ(％)≥: —
Ballistic|αkv(DVM)/J: —
Remark(20Mn6):
①, It is European standard in this table for lower temperature steel of Germany, and according to DIN-EN10028-1(2000)，DIN-EN10028-4(1994)，DIN-EN10222-3(1999)，DIN-EN10269(1999) etc.
②, The balance of Cr+Cu+Mo is under 0.50％.
Introduction low-temperature structural steel (20Mn6)
The total content of the alloy elements is 5% ~ 10%, and the microstructure depends on the heat treatment system. 9Ni steel is a typical steel type. There are two commonly used heat treatment systems. One is 900 tempered normalizing plus 790 tempering normalizing plus 570 tempering tempering, the other is 800 tempered water quenching plus 570 tempering. After quenching, the microstructure is low carbon horse low body. After normalizing, it is organized into low carbon martensite plus ferrite and a small amount of high carbon austenite. 9Ni steel has excellent toughness at low temperature under 196. The sensitivity of phosphorus to the tempering brittleness of 9Ni steel should be strictly controlled. 5Ni steel is mainly through the optimization of chemical composition and heat treatment method to control the three levels of organization, which is similar with the strength and toughness of 9Ni steel in 162 C and C 196 under low temperature.
The total content of alloying elements > 10%, for austenite, has very good toughness at low temperature, in 196 ~ 296 degrees Celsius temperature remains very high toughness. The chromium nickel austenite low temperature steel contains Cr18% and Ni9%, and the chromium free nickel austenite low temperature steel contains M23% to 26% and A1% - 4%, and the toughness of the low temperature steel is similar. It is generally used after solid solution treatment.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH,
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405,
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13, 20Mn6
The last：
14Ni6
Next up：
15NiCuMoNb5