We are a professional manufacturer of 1.1520, we can provide the third party inspection report and datasheet of 1.1520 as round bar, square bar, flat steel and so on. Please send the inquiry to us if you are if you are interested in 1.1520. We will serve you with honesty, integrity, and professional. The detail data as below follow:
Steel Grade: C70W1 | Material No.: 1.1520
CHEMICAL COMPOSITION(1.1520):
C(％) : 0.65～0.74
Si (％): 0.10～0.25
Mn(％): 0.10～0.25
P(％)≤: 0.03
S(％)≤: 0.03
HARDNESS AND HEAT TREATMENT(1.1520):
Hot Working/℃: 1000～800
Annealing/℃: 680～710
Quench/℃: 790～820
Refrigeration: Water
Hardness HRC: 63
Temper/℃: 180～300
Hardness After Annealing≤HBS|Bar: 190
Hardness After Annealing≤HBS|Plate: —
MECHANICAL PROPERTIES (1.1520):
Tensile Strength|σb≤MPa|Bar③: 640
Tensile Strength|σb≤MPa|Plate③: —
Remark(1.1520):
①, This hardness is fit for the round bar which Dia is under 12mm or the plate which thickness is under 5mm.
②, It can be used water quench under 780℃～820℃ if the Dia is big.
③, It is tensile strength after annealing.
Introduction Carbon Tool Steel(1.1520)
Tool steel refers to a variety of carbon and alloy steels that are particularly well-suited to be made into tools. Their suitability comes from their distinctive hardness, resistance to abrasion and deformation, and their ability to hold a cutting edge at elevated temperatures. As a result, tool steels are suited for use in the shaping of other materials.
Carbon tool steel has low production cost, convenient raw material source, easy cold and hot working, high hardness after heat treatment, and good wear resistance under low heating condition, so it has been widely applied. Among them, high quality carbon tool steel has high toughness and high degree of finish in grinding. It is suitable for making tools with complex shape and high precision. However, the hardness and wear resistance of this kind of steel decreased rapidly after the working temperature was more than 250 degrees C. This kind of steel has low hardenability and the tool section size is more than 15mm, and the surface layer is high in hardness after water quenching, so it can not be used as a large size tool. The quenching temperature of this kind of steel is narrow, easy to overheat, the distortion and cracking tendency of the quenching is great, and it is easy to produce soft spots.
Application(1.1520)
Tool steels are used for cutting, pressing, extruding, and coining of metals and other materials. Their use, such as the production of injection molds, is essential, due to their resistance to abrasion, which is an important criterion for a mold that will be used to produce hundreds of thousands of moldings of a product or part.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH, NAK80
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405,
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13, 1.1520
Steel Grade: C70W1 | Material No.: 1.1520
CHEMICAL COMPOSITION(1.1520):
C(％) : 0.65～0.74
Si (％): 0.10～0.25
Mn(％): 0.10～0.25
P(％)≤: 0.03
S(％)≤: 0.03
HARDNESS AND HEAT TREATMENT(1.1520):
Hot Working/℃: 1000～800
Annealing/℃: 680～710
Quench/℃: 790～820
Refrigeration: Water
Hardness HRC: 63
Temper/℃: 180～300
Hardness After Annealing≤HBS|Bar: 190
Hardness After Annealing≤HBS|Plate: —
MECHANICAL PROPERTIES (1.1520):
Tensile Strength|σb≤MPa|Bar③: 640
Tensile Strength|σb≤MPa|Plate③: —
Remark(1.1520):
①, This hardness is fit for the round bar which Dia is under 12mm or the plate which thickness is under 5mm.
②, It can be used water quench under 780℃～820℃ if the Dia is big.
③, It is tensile strength after annealing.
Introduction Carbon Tool Steel(1.1520)
Tool steel refers to a variety of carbon and alloy steels that are particularly well-suited to be made into tools. Their suitability comes from their distinctive hardness, resistance to abrasion and deformation, and their ability to hold a cutting edge at elevated temperatures. As a result, tool steels are suited for use in the shaping of other materials.
Carbon tool steel has low production cost, convenient raw material source, easy cold and hot working, high hardness after heat treatment, and good wear resistance under low heating condition, so it has been widely applied. Among them, high quality carbon tool steel has high toughness and high degree of finish in grinding. It is suitable for making tools with complex shape and high precision. However, the hardness and wear resistance of this kind of steel decreased rapidly after the working temperature was more than 250 degrees C. This kind of steel has low hardenability and the tool section size is more than 15mm, and the surface layer is high in hardness after water quenching, so it can not be used as a large size tool. The quenching temperature of this kind of steel is narrow, easy to overheat, the distortion and cracking tendency of the quenching is great, and it is easy to produce soft spots.
Application(1.1520)
Tool steels are used for cutting, pressing, extruding, and coining of metals and other materials. Their use, such as the production of injection molds, is essential, due to their resistance to abrasion, which is an important criterion for a mold that will be used to produce hundreds of thousands of moldings of a product or part.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH, NAK80
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405,
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13, 1.1520