P6
2018-04-10 18:33:17
We are a professional manufacturer of P6, we can provide the third party inspection report and datasheet of P6 as round bar, square bar, flat steel and so on. Please send the inquiry to us if you are if you are interested in P6. We will serve you with honesty, integrity, and professional. The detail data as below follow:
Steel Grade: ASTM P6| UNS: T51606
CHEMICAL COMPOSITION(P6):
C(％) : 0.05～0.15
Si(％) : 0.10～0.40
Mn(％) : 0.35～0.70
P(％)≤: 0.03
S(％)②: 0.03
Cr(％) : 1.25～1.75
Mo(％) : —
V(％) : —
W(％) : —
Other①: Ni3.25～3.75
HARDNESS AND HEAT TREATMENT (P6):
Hardness HBS|After Annealing: —
Hardness HBS|After Cold Drawing: —
Preheating Temperature/℃: —
Quenching/℃|Salt-bath Furnace: —
Quenching/℃|Controlled Atmosphere Furnace: —
Holding Time/min: —
Quenching Medium: —
Tempering/℃: —
Hardness≥HRC|After Tempering: 212
Remark(P6):
①, Residual elements content: Ni＋Cu≤0.75％.
②, A,D,H series to improve machinability, sulfur content can be increased to ω(S)0.06％～0.15％.
③, Increase the H13 sulfur, the upper limit of manganese content can reach ω(Mn)1.00%.
④, It also have Al which is ω(Al)1.05％～1.25％.
⑤, P20 and P21 usually to pre hardened state supplies.
⑥, After tempering hardness L2 refers to the hardness of ω(C)0.45％～0.55％.
⑦, It standard is ASTM A681-1999.
Please find the PDF for P6
Introduction Alloy Tool Steel (P6)
Alloy tool steel, carbon tool steel with Si, Mn, Ni, Cr, Mo, V, W and other alloy elements in order to improve the hardenability and toughness, wear resistance and heat resistance of steel.Add Cr and Mn can improve the hardenability of tool steel, according to the requirements, selectively to join or add other elements (adding amount is generally not more than 5%), that is, to form a series of alloy tool steel.It is mainly used in the manufacture of measuring tools and cutters, shock resistant and cold and hot mould and some special purpose tools.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH,
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405, P6
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13,
Steel Grade: ASTM P6| UNS: T51606
CHEMICAL COMPOSITION(P6):
C(％) : 0.05～0.15
Si(％) : 0.10～0.40
Mn(％) : 0.35～0.70
P(％)≤: 0.03
S(％)②: 0.03
Cr(％) : 1.25～1.75
Mo(％) : —
V(％) : —
W(％) : —
Other①: Ni3.25～3.75
HARDNESS AND HEAT TREATMENT (P6):
Hardness HBS|After Annealing: —
Hardness HBS|After Cold Drawing: —
Preheating Temperature/℃: —
Quenching/℃|Salt-bath Furnace: —
Quenching/℃|Controlled Atmosphere Furnace: —
Holding Time/min: —
Quenching Medium: —
Tempering/℃: —
Hardness≥HRC|After Tempering: 212
Remark(P6):
①, Residual elements content: Ni＋Cu≤0.75％.
②, A,D,H series to improve machinability, sulfur content can be increased to ω(S)0.06％～0.15％.
③, Increase the H13 sulfur, the upper limit of manganese content can reach ω(Mn)1.00%.
④, It also have Al which is ω(Al)1.05％～1.25％.
⑤, P20 and P21 usually to pre hardened state supplies.
⑥, After tempering hardness L2 refers to the hardness of ω(C)0.45％～0.55％.
⑦, It standard is ASTM A681-1999.
Please find the PDF for P6
Introduction Alloy Tool Steel (P6)
Alloy tool steel, carbon tool steel with Si, Mn, Ni, Cr, Mo, V, W and other alloy elements in order to improve the hardenability and toughness, wear resistance and heat resistance of steel.Add Cr and Mn can improve the hardenability of tool steel, according to the requirements, selectively to join or add other elements (adding amount is generally not more than 5%), that is, to form a series of alloy tool steel.It is mainly used in the manufacture of measuring tools and cutters, shock resistant and cold and hot mould and some special purpose tools.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH,
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405, P6
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13,