W6
2018-04-12 19:39:57
We are a professional manufacturer of W6, we can provide the third party inspection report and datasheet of W6 as round bar, square bar, flat steel and so on. Please send the inquiry to us if you are if you are interested in W6. We will serve you with honesty, integrity, and professional. The detail data as below follow:
Steel Grade: ASTM W6
Remark(W6):
①, It will be used this temperature if the ω(C) is between 0.50％～1.25％, it should be used the lower limit temperature if the ω(C) is between 1.25％～1.40％.
②, It will be used 740～760℃ if the ω(C) is between 0.60％～0.90％, it should be used 760～790℃ if the ω(C) is between 0.90％～1.40％.
③, It will be used 790～840℃ if the ω(C) is between 0.60％～0.80％, it should be used 770～840℃ if the ω(C) is between 0.85％～1.05％, it should be used 760～830℃ if the ω(C) is between 1.10％～1.40％.
④, The chemical composition which have parenthesis means Si＋Mn＋Cr≤0.75％.
⑤, The AISI W108、W109、W110、W112 are same as UNS T72301, the AISI W209、W210 are same as UNS T72302, the AISI W5 is same as UNS T72305.
⑥, The composition of P,S and residual elements is follow: P≤0.025％；S≤0.025％；Cu≤0.20％.
Please find the PDF for W6
Introduction Cemented Carbide (W6)
Cemented carbide is made of refractory metal hard compound and binding metal through powder metallurgy technology made of an alloy material.
Cemented carbide with high hardness, wear resistance, good strength and toughness, heat resistance, corrosion resistance and a series of excellent properties, especially its high hardness and wear resistance, even under the temperature of 500 ℃ is basic remains the same, there are still very high hardness at 1000 ℃.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH,
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405,
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13, W6
Steel Grade: ASTM W6
|
CHEMICAL COMPOSITION(W6): C(％) : ② Si(％) : 0.10～0.40 Mn(％) : 0.10～0.40 Cr(％): 0.03 V(％): 0.03 |
HARDNESS AND HEAT TREATMENT (W6): Initial Forging Temperature/℃: 980～1070① Finish Forging Temperature/℃: 820 Annealing/℃: 740～790② Hardness HBS|After Annealing : 163～202 Quenching/℃: 760～840③ Quenching Medium: Brine or Water Tempering/℃: 150～340 Hardness HBS|After Tempering: 65～50 |
①, It will be used this temperature if the ω(C) is between 0.50％～1.25％, it should be used the lower limit temperature if the ω(C) is between 1.25％～1.40％.
②, It will be used 740～760℃ if the ω(C) is between 0.60％～0.90％, it should be used 760～790℃ if the ω(C) is between 0.90％～1.40％.
③, It will be used 790～840℃ if the ω(C) is between 0.60％～0.80％, it should be used 770～840℃ if the ω(C) is between 0.85％～1.05％, it should be used 760～830℃ if the ω(C) is between 1.10％～1.40％.
④, The chemical composition which have parenthesis means Si＋Mn＋Cr≤0.75％.
⑤, The AISI W108、W109、W110、W112 are same as UNS T72301, the AISI W209、W210 are same as UNS T72302, the AISI W5 is same as UNS T72305.
⑥, The composition of P,S and residual elements is follow: P≤0.025％；S≤0.025％；Cu≤0.20％.
Please find the PDF for W6
Introduction Cemented Carbide (W6)
Cemented carbide is made of refractory metal hard compound and binding metal through powder metallurgy technology made of an alloy material.
Cemented carbide with high hardness, wear resistance, good strength and toughness, heat resistance, corrosion resistance and a series of excellent properties, especially its high hardness and wear resistance, even under the temperature of 500 ℃ is basic remains the same, there are still very high hardness at 1000 ℃.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH,
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405,
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13, W6