T30403
2018-04-14 20:39:28
We are a professional manufacturer of T30403, we can provide the third party inspection report and datasheet of T30403 as round bar, square bar, flat steel and so on. Please send the inquiry to us if you are if you are interested in T30403. We will serve you with honesty, integrity, and professional. The detail data as below follow:
Steel Grade: ASTM D3| UNS: T30403
Remark(T30403):
①, Residual elements content: Ni＋Cu≤0.75％.
②, A,D,H series to improve machinability, sulfur content can be increased to ω(S)0.06％～0.15％.
③, Increase the H13 sulfur, the upper limit of manganese content can reach ω(Mn)1.00%.
④, It also have Al which is ω(Al)1.05％～1.25％.
⑤, P20 and P21 usually to pre hardened state supplies.
⑥, After tempering hardness L2 refers to the hardness of ω(C)0.45％～0.55％.
⑦, It standard is ASTM A681-1999.
Please find the PDF for T30403
Introduction Alloy Tool Steel (T30403)
Alloy tool steel, carbon tool steel with Si, Mn, Ni, Cr, Mo, V, W and other alloy elements in order to improve the hardenability and toughness, wear resistance and heat resistance of steel.Add Cr and Mn can improve the hardenability of tool steel, according to the requirements, selectively to join or add other elements (adding amount is generally not more than 5%), that is, to form a series of alloy tool steel.It is mainly used in the manufacture of measuring tools and cutters, shock resistant and cold and hot mould and some special purpose tools.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH,
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405, T30403
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13,
Steel Grade: ASTM D3| UNS: T30403
|
CHEMICAL COMPOSITION(T30403): C(％) : 2.00～2.35 Si(％) : 0.10～0.60 Mn(％) : 0.20～0.60 P(％)≤: 0.03 S(％)②: 0.03 Cr(％) : 11.0～13.5 Mo(％) : — V(％) : ≤1.00 W(％) : ≤1.00 Other①: — |
HARDNESS AND HEAT TREATMENT (T30403): Hardness HBS|After Annealing: 255 Hardness HBS|After Cold Drawing: 269 Preheating Temperature/℃: 816 Quenching/℃|Salt-bath Furnace: 954 Quenching/℃|Controlled Atmosphere Furnace: 968 Holding Time/min: 10～20 Quenching Medium: Oil Cooling Tempering/℃: 204 Hardness≥HRC|After Tempering: 61 |
①, Residual elements content: Ni＋Cu≤0.75％.
②, A,D,H series to improve machinability, sulfur content can be increased to ω(S)0.06％～0.15％.
③, Increase the H13 sulfur, the upper limit of manganese content can reach ω(Mn)1.00%.
④, It also have Al which is ω(Al)1.05％～1.25％.
⑤, P20 and P21 usually to pre hardened state supplies.
⑥, After tempering hardness L2 refers to the hardness of ω(C)0.45％～0.55％.
⑦, It standard is ASTM A681-1999.
Please find the PDF for T30403
Introduction Alloy Tool Steel (T30403)
Alloy tool steel, carbon tool steel with Si, Mn, Ni, Cr, Mo, V, W and other alloy elements in order to improve the hardenability and toughness, wear resistance and heat resistance of steel.Add Cr and Mn can improve the hardenability of tool steel, according to the requirements, selectively to join or add other elements (adding amount is generally not more than 5%), that is, to form a series of alloy tool steel.It is mainly used in the manufacture of measuring tools and cutters, shock resistant and cold and hot mould and some special purpose tools.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH,
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405, T30403
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13,