We are a professional manufacturer of T61202, we can provide the third party inspection report and datasheet of T61202 as round bar, square bar, flat steel and so on. Please send the inquiry to us if you are if you are interested in T61202. We will serve you with honesty, integrity, and professional. The detail data as below follow:
Steel Grade: ASTM L2| UNS: T61202
Remark(T61202):
①, Residual elements content: Ni＋Cu≤0.75％.
②, A,D,H series to improve machinability, sulfur content can be increased to ω(S)0.06％～0.15％.
③, Increase the H13 sulfur, the upper limit of manganese content can reach ω(Mn)1.00%.
④, It also have Al which is ω(Al)1.05％～1.25％.
⑤, P20 and P21 usually to pre hardened state supplies.
⑥, After tempering hardness L2 refers to the hardness of ω(C)0.45％～0.55％.
⑦, It standard is ASTM A681-1999.
Please find the PDF for T61202
Introduction Alloy Tool Steel (T61202)
Alloy tool steel, carbon tool steel with Si, Mn, Ni, Cr, Mo, V, W and other alloy elements in order to improve the hardenability and toughness, wear resistance and heat resistance of steel.Add Cr and Mn can improve the hardenability of tool steel, according to the requirements, selectively to join or add other elements (adding amount is generally not more than 5%), that is, to form a series of alloy tool steel.It is mainly used in the manufacture of measuring tools and cutters, shock resistant and cold and hot mould and some special purpose tools.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH,
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405, T61202
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13,
Steel Grade: ASTM L2| UNS: T61202
|
CHEMICAL COMPOSITION(T61202): C(％) : 0.45～1.00 Si(％) : 0.10～0.50 Mn(％) : 0.10～0.90 P(％)≤: 0.03 S(％)②: 0.03 Cr(％) : 0.70～1.20 Mo(％) : ≤0.25 V(％) : 0.10～0.30 W(％) : — Other①: — |
HARDNESS AND HEAT TREATMENT (T61202): Hardness HBS|After Annealing: 197 Hardness HBS|After Cold Drawing: 241 Preheating Temperature/℃: 649 Quenching/℃|Salt-bath Furnace: 857 Quenching/℃|Controlled Atmosphere Furnace: 871 Holding Time/min: 5～15 Quenching Medium: Oil Cooling Tempering/℃: 204 Hardness≥HRC|After Tempering: 53 |
①, Residual elements content: Ni＋Cu≤0.75％.
②, A,D,H series to improve machinability, sulfur content can be increased to ω(S)0.06％～0.15％.
③, Increase the H13 sulfur, the upper limit of manganese content can reach ω(Mn)1.00%.
④, It also have Al which is ω(Al)1.05％～1.25％.
⑤, P20 and P21 usually to pre hardened state supplies.
⑥, After tempering hardness L2 refers to the hardness of ω(C)0.45％～0.55％.
⑦, It standard is ASTM A681-1999.
Please find the PDF for T61202
Introduction Alloy Tool Steel (T61202)
Alloy tool steel, carbon tool steel with Si, Mn, Ni, Cr, Mo, V, W and other alloy elements in order to improve the hardenability and toughness, wear resistance and heat resistance of steel.Add Cr and Mn can improve the hardenability of tool steel, according to the requirements, selectively to join or add other elements (adding amount is generally not more than 5%), that is, to form a series of alloy tool steel.It is mainly used in the manufacture of measuring tools and cutters, shock resistant and cold and hot mould and some special purpose tools.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH,
ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400,
X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321,
NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418,
616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405, T61202
ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13,