We are a professional manufacturer of UNS T11330, we can provide the third party inspection report and datasheet of UNS T11330 as round bar, square bar, flat steel and so on. Please send the inquiry to us if you are if you are interested in UNS T11330. We will serve you with honesty, integrity, and professional. The detail data as below follow:
Steel Grade: ASTM M30| UNS T11330| Type: Molybdenum Series
Remark(UNS T11330):
①, ω(Cu+Ni)≤0.75%
②, The composition of S can be increased to ω(S)0.06%~0.15% in order to improve the performance of cutting.
③, The standard is ASTM A600-1999.
Please find the PDF for UNS T11330
Introduction High Speed Tool Steel (UNS T11330)
High speed tool steel is mainly used in manufacturing high efficient cutting tool.Due to its high red hardness, good abrasion resistance, high strength characteristics, and also used in the manufacture of high performance requirements of the mould, and hot spring roll, high temperature bearing, etc.The use of high speed tool steel after heat treatment the hardness can reach more than HRC63, under the working temperature of 600 ℃ can still maintain a high hardness, but its toughness, wear resistance and heat resistance are good.Annealing state of high speed tool steel main alloy elements tungsten, molybdenum, chromium, vanadium, and some joined the cobalt in high speed tool steel, aluminum and other elements.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH, ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400, X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321, NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418, 616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405, ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13, UNS T11330
Steel Grade: ASTM M30| UNS T11330| Type: Molybdenum Series
CHEMICAL COMPOSITION(UNS T11330): C(%) : 0.75~0.85 Si(%) : 0.20~0.45 Mn(%) : 0.15~0.40 P(%)≤ : 0.03 S(%)≤② : 0.03 Cr(%) : 3.50~4.25 Mo(%) : 7.75~9.00 V(%) : 1.00~1.40 W(%) : 1.30~2.30 Co(%): 4.50~5.50 |
HARDNESS AND HEAT TREATMENT (UNS T11330): Hardness HBS|Annealing: 269 Hardness HBS|Cold Drawing: 285 Hardness HBS|Annealing after Cold Drawing: 277 Preheating Temperature/℃: 732~843 Quenching/℃|Salt-Bath Furnace: 1204 Quenching/℃|Controlled Atmosphere Furnace: 1216 Tempering/℃: 552 Hardness≥HRC|After Tempering: 64 |
①, ω(Cu+Ni)≤0.75%
②, The composition of S can be increased to ω(S)0.06%~0.15% in order to improve the performance of cutting.
③, The standard is ASTM A600-1999.
Please find the PDF for UNS T11330
Introduction High Speed Tool Steel (UNS T11330)
High speed tool steel is mainly used in manufacturing high efficient cutting tool.Due to its high red hardness, good abrasion resistance, high strength characteristics, and also used in the manufacture of high performance requirements of the mould, and hot spring roll, high temperature bearing, etc.The use of high speed tool steel after heat treatment the hardness can reach more than HRC63, under the working temperature of 600 ℃ can still maintain a high hardness, but its toughness, wear resistance and heat resistance are good.Annealing state of high speed tool steel main alloy elements tungsten, molybdenum, chromium, vanadium, and some joined the cobalt in high speed tool steel, aluminum and other elements.
HOT SALE:
SA-675GR70, SA-387GR91, X6NiCrTiMoVB25-15-2, 17-4PH, 15-5PH, ASTM 630, X3CrNiMo13-4, UNS41500, X10CrNiTi18-10, S17400, X5CrNiCuNbl6-4, 316Ti, 301A, 303, 304L, 310S, 316L, 317L, 321, NKA80, DIN 1.4731, DIN 1.4021, DIN 1.4016, DIN 1.4571, DIN 1.4418, 616, 440B, 440C, 431, 430FR, 430F, 430, 422, 416, 410, 405, ASTM D2, X155CrMoV12-1, ASTM D3, AISI H11, AISI H13, UNS T11330